Polishing method and polishing apparatus

ABSTRACT

The present invention relates to a polishing method and apparatus for polishing a workpiece such as a semiconductor wafer to a flat mirror finish. A polishing liquid Q is supplied onto a polishing cloth  11  attached on a turntable  1 , and a semiconductor wafer W to be polished is held by a top ring  2.  The turntable  1  and the top ring  2  are rotated, respectively. A surface, to be polished, of the semiconductor wafer W held by the top ring  2  is pressed against the polishing cloth  11  on the turntable  1  to polish the semiconductor wafer W. When the polished semiconductor wafer W held by said top ring  2  is to be removed from the polishing cloth  11  on the turntable  1,  a relative speed of the turntable  1  and the top ring  2  is increased in comparison with a relative speed of the turntable  1  and the top ring  2  at a period of polishing.

BACKGROUND OF THE INVENTION

[0001] 1. Field of the Invention

[0002] The present invention relates to a polishing method and apparatus, and more particularly to a polishing method and apparatus for polishing a workpiece such as a semiconductor wafer to a flat mirror finish.

[0003] 2. Description of the Related Art

[0004] Recent rapid progress in semiconductor device integration demands smaller and smaller wiring patterns or interconnections and also narrower spaces between interconnections which connect active areas. One of the processes available for forming such interconnection is photolithography. Although the photolithographic process can form interconnections that are at most 0.5 μm wide, it requires that surfaces on which pattern images are to be focused by a stepper be as flat as possible because the depth of focus of the optical system is relatively small. However, conventional apparatuses for planarizing semiconductor wafers (substrate-like workpieces), such as self-planarizing CVD apparatus or etching apparatus, fail to produce completely planarized surfaces on semiconductor wafers. Recently, it has been attempted to planarize semiconductor wafers with a polishing apparatus which is expected to achieve easily complete planarization of the semiconductor wafers as compared with the above conventional apparatuses. Such a process is called Chemical Mechanical Polishing (CMP) in which the semiconductor wafers are chemically and mechanically polished while supplying a polishing liquid comprising abrasive particles and chemical solution such as alkaline solution.

[0005]FIG. 1 is a schematic view showing the basic structure of this type of polishing apparatus. As shown in FIG. 1, the polishing apparatus has a turntable 1 with a polishing cloth 11 attached thereon and constituting a polishing surface, and a top ring 2 for holding a semiconductor wafer (workpiece) W in such a manner that the surface, to be polished, of the semiconductor wafer W faces the turntable 1. The top ring 2 is connected to a lower end of a top ring shaft 3 via a ball joint 4 so as to be tiltable with respect to the top ring shaft 3. The semiconductor wafer W to be polished is pressed against the turntable 1 under a certain pressure by the top ring 2 while the turntable 1 and the top ring 2 are independently being rotated, and the surface of the semiconductor wafer W is polished to a flat mirror finish while a polishing liquid Q is being supplied from a polishing liquid supply nozzle 5. In this case, the surface, to be polished, of the semiconductor wafer W is brought into sliding contact with the upper surface of the polishing cloth 11 while following the inclination of the upper surface of the polishing cloth 11 via the ball joint 4.

[0006] As a polishing cloth attached on a turntable, a polishing cloth made of non-woven fabric has heretofore been employed. Higher levels of integration achieved in recent years for ICs and LSI circuits demand smaller steps or surface irregularities on the polished surface of the semiconductor wafer. In order to meet such a demand, there has been used a polishing cloth made of a hard material such as polyurethane foam.

[0007] After the semiconductor wafer W is polished by the polishing apparatus, it is necessary to remove the semiconductor wafer W from the polishing surface (the polishing cloth 11 ) on the turntable 1. However, a large surface tension acts between the polishing cloth 11 and the semiconductor wafer W due to the polishing liquid Q interposed therebetween. Accordingly, if the top ring 2 holding the semiconductor wafer W is lifted at the polishing position in order to remove the semiconductor wafer W from the polishing cloth 11, there are some cases that only the top ring 2 is lifted and the semiconductor wafer W adheres to the polishing cloth 11 to be left on the polishing cloth 11.

[0008] Such a problem can be solved by an overhanging action of the top ring. In the overhanging action, after the polishing process is completed, the top ring 2 is not lifted at the polishing position, but is moved to the outer circumferential edge of the polishing cloth 11 to partly expose the polished surface of the semiconductor wafer W beyond the outer circumferential edge of the polishing cloth 11 and then lifted to remove the semiconductor wafer W from the polishing cloth 11. This overhanging action allows the surface tension between the polishing cloth 11 and the semiconductor wafer W to be reduced, and the semiconductor wafer W can reliably be separated or removed from the polishing cloth 11.

[0009] As described above, with the overhanging action, the surface tension between the polishing cloth 11 and the semiconductor wafer W can be reduced. However, the top ring 2 may tilt when the polished semiconductor wafer W projects from the outer circumferential edge of the polishing cloth 11. In this case, the semiconductor wafer W is intensively pressed at the outer circumferential edge of the polishing cloth 11, so that the semiconductor wafer W is cracked or scratched.

[0010] The polishing capability of the polishing cloth is gradually deteriorated due to a deposit of abrasive particles and ground-off particles of the semiconductor material, and due to changes in the characteristics of the polishing cloth. Therefore, if the same polishing cloth is used to repeatedly polish semiconductor wafers, the polishing rate of the polishing apparatus is lowered, and the polished semiconductor wafers tend to suffer polishing irregularities. Therefore, it has been customary to condition the polishing cloth according to a process called “dressing” for recovering the surface of the polishing cloth with a diamond dresser or the like before, or after, or during polishing.

[0011] When the diamond dresser dresses the polishing surface of the polishing cloth 11, it scrapes a thin layer off the polishing cloth 11. Therefore, after the polishing surface of the polishing cloth has been dressed many times, it becomes irregular, i.e., loses its planarity, causing formation of steps. As a result, during the movement of the polished semiconductor wafer W to the outer circumferential edge of the polishing cloth 11 in the aforementioned overhanging action, the semiconductor wafer W may be cracked or scratched because of the irregularities of the polishing cloth 11.

SUMMARY OF THE INVENTION

[0012] The present invention has been made in view of the above drawbacks. It is therefore an object of the present invention to provide a polishing method and apparatus which can easily and safely remove a polished workpiece from a polishing surface, and can increase a throughput.

[0013] According to an aspect of the present invention, there is provided a polishing method comprising: rotating a turntable having a polishing surface thereon, and a top ring for holding a workpiece to be polished, respectively; pressing a surface, to be polished, of the workpiece held by the top ring against the polishing surface on the turntable to polish the workpiece; and increasing a relative speed of the turntable and the top ring when the polished workpiece held by the top ring is to be removed from the polishing surface on the turntable, in comparison with a relative speed of the turntable and the top ring at a period of polishing.

[0014] According to a preferred aspect of the present invention, a rotational speed of the turntable is increased in comparison with a rotational speed of the turntable at a period of polishing to increase the relative speed of the turntable and the top ring.

[0015] According to another preferred aspect of the present invention, rotational speeds of the turntable and the top ring are respectively increased in comparison with rotational speeds of the turntable and the top ring at a period of polishing to increase the relative speed of the turntable and the top ring.

[0016] According to another aspect of the present invention, there is provided a polishing apparatus for polishing a workpiece to be polished, comprising: a turntable having a polishing surface thereon; a top ring for holding the workpiece to be polished and pressing the workpiece against the polishing surface on the turntable; a motor for rotating the turntable; and a controller for controlling a rotational speed of the motor; wherein when the polished workpiece held by the top ring is to be removed from the polishing surface on the turntable, the motor increases a rotational speed of the turntable in comparison with a rotational speed of the turntable at a period of polishing.

[0017] According to still another aspect of the present invention, there is provided a polishing apparatus for polishing a workpiece to be polished, comprising: a turntable having a polishing surface thereon; a top ring for holding the workpiece to be polished and pressing the workpiece against the polishing surface on the turntable; a motor for rotating the top ring; and a controller for controlling a rotational speed of the motor; wherein when the polished workpiece held by the top ring is to be removed from the polishing surface on the turntable, the motor increases a rotational speed of the top ring in comparison with a rotational speed of the top ring at a period of polishing.

[0018] According to another aspect of the present invention, there is provided a polishing method comprising: moving a polishing surface and a top ring for holding a workpiece to be polished relative to each other; pressing a surface, to be polished, of the workpiece held by the top ring against the polishing surface to polish the workpiece; and increasing a relative speed of the polishing surface and the top ring when the polished workpiece held by the top ring is to be removed from the polishing surface, in comparison with a relative speed of the polishing surface and the top ring at a period of polishing.

[0019] It is desirable that the rotational speed of the turntable be increased to 100 min⁻¹ or larger, and the rotational speed of the top ring be increased to 75 min⁻¹ or larger.

[0020] According to the present invention, the liquid film thickness of a polishing liquid on the polishing surface is decreased by the action of the centrifugal force, so that the surface tension due to the polishing liquid is reduced. Therefore, even if the top ring is lifted at the polishing position without an overhanging action, the workpiece can easily be removed from the polishing surface. Thus, the present invention can prevent the workpiece from being left on the polishing surface and being cracked or scratched. Further, since it is not necessary to perform the overhanging action, tact time for polishing can be reduced to increase a throughput. Furthermore, when the rotational speed of the turntable is increased, the components of the polishing liquid are scattered and discharged from the upper surface of the turntable by the action of the centrifugal force. Accordingly, it becomes easier to remove the workpiece from the polishing surface, and simultaneously the polishing conditions for the next workpiece to be polished can be arranged to be preferred conditions. As a result, the throughput can be increased.

[0021] The above and other objects, features, and advantages of the present invention will be apparent from the following description when taken in conjunction with the accompanying drawings which illustrates preferred embodiments of the present invention by way of example.

BRIEF DESCRIPTION OF THE DRAWINGS

[0022]FIG. 1 is a schematic view showing the basic structure of a polishing apparatus;

[0023]FIG. 2 is a front view showing the whole structure of a polishing apparatus according to an embodiment of the present invention; and

[0024]FIG. 3 is a schematic view showing a mechanism for vacuum attraction of a wafer according to an embodiment of the present invention;

[0025]FIGS. 4A and 4B are schematic views showing an overhanging action; and

[0026]FIG. 5 is a schematic view showing a polishing apparatus according to another embodiment of the present invention.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0027] A polishing method and apparatus according to an embodiment of the present invention will be described below with reference to FIG. 2. FIG. 2 is a front view showing the whole structure of a polishing apparatus according to an embodiment of the present invention. In FIG. 2, like parts and components are designated by the same reference numerals and characters as those shown in FIG. 1.

[0028] As shown in FIG. 2, the polishing apparatus according to the present embodiment comprises a turntable 1, a polishing liquid supply nozzle 5, and a top ring unit 6. The turntable 1 has a vertical shaft 13 coupled to a motor 12 disposed below the turntable 1 and is rotatable about the shaft 13, as indicated by an arrow in FIG. 1. The motor 12 is connected to a controller 14 for controlling a rotational speed of the motor 12. A polishing cloth 11 is attached on an upper surface of the turntable 1. The polishing cloth 11 has an upper polishing surface held in sliding contact with a semiconductor wafer W (workpiece) to be polished. The polishing liquid supply nozzle 5 is disposed above the turntable 1, and a polishing liquid Q is supplied onto the polishing cloth 11 of the turntable 1 from the polishing liquid supply nozzle 5.

[0029] In the present embodiment, as described above, the turntable 1 has the polishing cloth 11 attached thereon. However, the turntable 1 is not limited to the above one, and the turntable 1 may comprise a polishing plate of a fixed abrasive, for example. The fixed abrasive comprises abrasive particles fixed by a binder.

[0030] As shown in FIG. 2, the top ring unit 6 mainly comprises a swing shaft 61, an arm-shaped top ring head 62 connected to the swing shaft 61, and a top ring 2 connected to a top ring shaft 3 extended downwardly from the top ring head 62. The top ring head 62 is swingable in a horizontal plane by rotation of the swing shaft 61. The top ring 2 is connected to the lower end of the top ring shaft 3 via a ball joint 4 so as to be tiltable with respect to the top ring shaft 3.

[0031] The top ring 2 of the top ring unit 6 has, on a lower surface thereof, an elastic pad 21 formed of polyurethane or the like. The semiconductor wafer W is attracted to a lower surface of the elastic pad 21 under a vacuum in such a state that the semiconductor wafer W is brought into contact with the lower surface of the elastic pad 21, so that the semiconductor wafer W is held by the top ring 2. The top ring 2 has a cylindrical guide ring 22 at an outer circumferential edge of a lower portion thereof. A lower portion of the guide ring 22 protrudes from the top ring 2, and hence a recess is formed at the radially inner side of the lower portion of the guide ring 22. The semiconductor wafer W is held in the recess for preventing the semiconductor wafer W from being dislodged from the lower surface of the top ring 2 during the polishing process.

[0032] The top ring 2 is coupled to a motor 63 provided in the top ring head 62 via the top ring shaft 3, and is rotatable about the top ring shaft 3. The motor 63 is connected to a controller 63 a for controlling a rotational speed of the motor 63. The top ring 2 is also coupled to a lifting/lowering cylinder 64 via the top ring shaft 3, and is vertically movable for pressing the semiconductor wafer W held in the top ring 2 against the polishing cloth 11 under a predetermined pressure.

[0033] In the polishing apparatus thus constructed, the semiconductor wafer W held on the lower surface of the elastic pad 21 attached on the lower surface of the top ring 2 is pressed against the polishing cloth 11 on the turntable 1, while the polishing liquid Q is being supplied onto the polishing cloth 11 of the turntable 1 from the polishing liquid supply nozzle 5. The turntable 1 and the top ring 2 are independently rotated, so that the polishing cloth 11 and the semiconductor wafer W are moved relative to each other. For example, a suspension of fine polishing particles of silica or the like in an alkali solution is used as the polishing liquid supplied from the polishing liquid nozzle 5. Thus, the semiconductor wafer W is polished to a flat mirror finish by the combined effect of a chemical polishing effect attained by the alkali and a mechanical polishing effect attained by the polishing particles.

[0034] The semiconductor wafer W is polished in the above manner. After the polishing process of the semiconductor wafer W is completed, it is necessary to separate or remove the semiconductor wafer W from the polishing cloth 11 on the turntable 1. In this case, the surface tension acts between the polishing cloth 11 and the semiconductor wafer W, as described above. According to the present invention, when the semiconductor wafer W is to be separated or removed from the polishing cloth 11, the rotational speeds of the turntable 1 and the top ring 2 are increased by the motor 12 and the motor 63 in comparison with their rotational speeds at a period of the polishing process. As a result, reduction of the surface tension can be achieved as follows:

[0035] Specifically, when the rotational speeds of the turntable 1 and the top ring 2 are increased, the liquid film thickness of the polishing liquid Q on the polishing cloth 11 is decreased by the action of the centrifugal force, so that the surface tension due to the polishing liquid Q is reduced. Therefore, even if the top ring 2 is lifted at the polishing position without an overhanging action, the semiconductor wafer W can easily be removed from the polishing cloth 11. Thus, the present invention can prevent the semiconductor wafer W from being left on the polishing cloth 11 and being cracked or scratched. Further, since it is not necessary to perform the overhanging action, tact time for polishing can be reduced to increase a throughput. Furthermore, when the rotational speed of the turntable 1 is increased by the motor 12, the components of the polishing liquid are scattered and discharged from the upper surface of the turntable 1 by the action of the centrifugal force. Accordingly, it becomes easier to remove the semiconductor wafer from the polishing surface, and simultaneously the polishing conditions for the next semiconductor wafer to be polished can be arranged to be preferred conditions. As a result, the throughput can be increased.

[0036] In the present embodiment, as shown in FIG. 3, a vacuum line 8 communicating with a vacuum evacuation source 7 is connected to the top ring 2. The top ring 2 has a chamber (or a space) 2 a connected to the vacuum line 8, and a plurality of holes 2 b communicating with the chamber 2 a and being open to the lower surface of the top ring 2. Thus, the semiconductor wafer W is held on the lower surface of the top ring 2 by vacuum attraction. When the semiconductor wafer W is to be removed from the polishing cloth 11, the top ring 2 is mechanically lifted. If the semiconductor wafer w is dislodged from the top ring 2 and is left on the polishing cloth 11, the pressure of the vacuum line 8 changes from a vacuum nearer to the atmospheric pressure. Therefore, the pressure of the vacuum line 8 is monitored to judge whether the semiconductor wafer W has normally been removed from the polishing cloth 11 or not.

[0037] In the present embodiment, as shown in FIG. 3, a vacuum pressure sensor 9 is provided in the vacuum line 8 to measure and monitor the pressure of the vacuum line 8, for thereby judging whether the semiconductor wafer W has normally been removed from the polishing cloth 11 or not. Specifically, after the lifting operation of the top ring 2 is started, the pressure of the vacuum line 8 is measured with the vacuum pressure sensor 9. If the measured value is less than a predetermined pressure value, it is judged that the semiconductor wafer W has normally been removed from the polishing cloth 11 in such a state that the semiconductor wafer W is attracted to the top ring 2. More specifically, if pressures that are 10 kPa or more larger than the predetermined pressure value, at which the semiconductor wafer W is judged to be normally attracted to the top ring 2, are measured for a predetermined period or longer, then it is judged that the semiconductor wafer W has been dislodged from the top ring 2.

[0038] Experiments were carried out as follows:

[0039] A strain gauge was provided in the top ring, and the rotational speeds of the turntable and the top ring were respectively changed when the semiconductor wafer was to be removed from the polishing cloth. An axial force acting on the top ring at this time, i.e., a force for lifting the top ring, was measured.

[0040] A top ring for holding a semiconductor wafer having a diameter of 200 mm was used.

[0041] Dressing was performed for 600 seconds by a dresser before a polishing process.

[0042] After three semiconductor wafers were polished as dummies to obtain the normal condition of the polishing cloth, two semiconductor wafers were polished for measuring a force for lifting the top ring. The force for lifting the top ring was calculated based on the average of the values measured after polishing of the two semiconductor wafers.

[0043] During the polishing process, the rotational speed of the turntable was 22 min⁻¹, and the rotational speed of the top ring was 16 min⁻¹.

[0044] When the semiconductor wafer was lifted, the rotational speed of the turntable was changed to 50 min⁻¹, 75 min⁻¹ or 100 min⁻¹, and the rotational speed of the top ring was changed to 55 min⁻¹ or 75 min⁻¹.

[0045] As the dresser, a new dresser and a used dresser that had already used for processing 17,000 semiconductor wafers were used in the experiments, respectively.

[0046] The measurement results in the above experiments are shown in Table 1. TABLE 1 Force for Force for Rotational lifting top lifting top speed of Rotational ring in the ring in the turntable speed of top case of new case of used (min⁻¹) ring (min⁻¹) dresser (N) dresser (N) 50 55 332.1 342 75 55 99.9 378.9 100 55 378 185.4 50 75 389.7 300.9 75 75 338.7 178.8 100 75 25.9 96.6

[0047] From Table 1, it is shown that, in both cases of the new dresser and the used dresser, when the rotational speed of the turntable and the rotational speed of the top ring at a period of lifting a semiconductor wafer were the largest, i.e., when the rotational speed of the turntable was 100 min⁻¹, and the rotational speed of the top ring 75 min⁻¹, the force for lifting the top ring was the lowest. In this case, the semiconductor wafer W could easily be lifted from the polishing cloth 11.

[0048] In the present embodiment, the top ring 2 is lifted at the polishing position without an overhanging action. However, the top ring 2 may perform an overhanging action after the polishing process, as shown in FIGS. 4A and 4B. After the polishing process is completed, the top ring 2 is moved to the outer circumferential edge of the polishing cloth 11 to partly expose the polished surface of the semiconductor wafer W beyond the outer circumferential edge of the polishing cloth 11 and then lifted to remove the semiconductor wafer W from the polishing cloth 11. When the semiconductor wafer W is to be separated or removed from the polishing cloth 11, the rotational speed of the top ring 2 is increased in comparison with the rotational speed at a period of the polishing process. The liquid film thickness of the polishing liquid on the polishing cloth 11 is decreased by the action of the centrifugal force, so that the surface tension due to the polishing liquid is reduced by the synergistic effect of the centrifugal force and the overhanging action. Therefore, the semiconductor wafer W can more easily be removed from the polishing surface. As a result, the semiconductor wafer W can be prevented from being left on the polishing surface 18 more effectively.

[0049] In the present embodiment, the polishing surface is rotated to polish the semiconductor wafer. However, the polishing surface and the top ring may be moved relative to each other. In FIG. 5, a polishing surface is constituted by a belt 15 having abrasive particles on its surface. The belt 15 is wound on two rotatable drums 16, 17. The drums 16, 17 are rotated to linearly move the belt 15 along an arrow A. A support 18 is disposed between an upper belt surface 15 a and a lower belt surface 15 b. A semiconductor wafer held by the top ring 2 is pressed against the belt 15 and the support 18. Thus, the semiconductor wafer is polished. When the semiconductor wafer is to be separated or removed from the belt 15, the rotational speed of the top ring 2 is increased in comparison with the rotational speed at a period of the polishing process. As in the case of the aforementioned embodiment, the semiconductor wafer can be prevented from being left on the belt 15 (polishing surface).

[0050] As described above, according to the present invention, when a polished workpiece held by a top ring is to be removed from a polishing surface on a turntable, a rotational speed of the turntable is increased in comparison with a rotational speed of the turntable at a period of polishing. A relative speed of the turntable and the top ring is increased in comparison with a relative speed of the turntable and the top ring at a period of polishing. Hence, even if the top ring is lifted at the polishing position without an overhanging action, the workpiece can easily be removed from the polishing surface. Thus, the present invention can prevent the workpiece from being left on the polishing surface and being cracked or scratched. Further, since it is not necessary to perform the overhanging action, tact time for polishing can be reduced to increase a throughput. Furthermore, when the rotational speed of the turntable is increased, the components of the polishing liquid are scattered and discharged from the upper surface of the turntable by the action of the centrifugal force. Accordingly, it becomes easier to remove the workpiece from the polishing surface, and simultaneously the polishing conditions for the next workpiece to be polished can be arranged to be preferred conditions. As a result, the throughput can be increased.

[0051] Although certain preferred embodiments of the present invention have been shown and described in detail, it should be understood that various changes and modifications may be made therein without departing from the scope of the appended claims. 

What is claimed is:
 1. A polishing method comprising: rotating a turntable having a polishing surface thereon, and a top ring for holding a workpiece to be polished, respectively; pressing a surface, to be polished, of said workpiece held by said top ring against said polishing surface on said turntable to polish said workpiece; and increasing a relative speed of said turntable and said top ring when said polished workpiece held by said top ring is to be removed from said polishing surface on said turntable, in comparison with a relative speed of said turntable and said top ring at a period of polishing.
 2. A polishing method according to claim 1, wherein a rotational speed of said turntable is increased in comparison with a rotational speed of said turntable at a period of polishing to increase said relative speed of said turntable and said top ring.
 3. A polishing method according to claim 2, wherein said rotational speed of said turntable is increased to 100 min⁻¹ or larger.
 4. A polishing method according to claim 1, wherein rotational speeds of said turntable and said top ring are respectively increased in comparison with rotational speeds of said turntable and said top ring at a period of polishing to increase said relative speed of said turntable and said top ring.
 5. A polishing method according to claim 4, wherein said rotational speed of said top ring is increased to 75 min⁻¹ or larger.
 6. A polishing method according to claim 5, wherein said rotational speed of said turntable is increased to 100 min⁻¹ or larger.
 7. A polishing apparatus for polishing a workpiece to be polished, comprising: a turntable having a polishing surface thereon; a top ring for holding said workpiece to be polished and pressing said workpiece against said polishing surface on said turntable; a motor for rotating said turntable; and a controller for controlling a rotational speed of said motor; wherein when said polished workpiece held by said top ring is to be removed from said polishing surface on said turntable, said motor increases a rotational speed of said turntable in comparison with a rotational speed of said turntable at a period of polishing.
 8. A polishing apparatus according to claim 7, wherein said motor increases said rotational speed of said turntable to 100 min⁻¹ or larger.
 9. A polishing apparatus for polishing a workpiece to be polished, comprising: a turntable having a polishing surface thereon; a top ring for holding said workpiece to be polished and pressing said workpiece against said polishing surface on said turntable; a motor for rotating said top ring; and a controller for controlling a rotational speed of said motor; wherein when said polished workpiece held by said top ring is to be removed from said polishing surface on said turntable, said motor increases a rotational speed of said top ring in comparison with a rotational speed of said top ring at a period of polishing.
 10. A polishing apparatus according to claim 9, wherein said motor increases said rotational speed of said top ring to 75 min⁻¹ or larger.
 11. A polishing method comprising: moving a polishing surface and a top ring for holding a workpiece to be polished relative to each other; pressing a surface, to be polished, of said workpiece held by said top ring against said polishing surface to polish said workpiece; and increasing a relative speed of said polishing surface and said top ring when said polished workpiece held by said top ring is to be removed from said polishing surface, in comparison with a relative speed of said polishing surface and said top ring at a period of polishing. 